Improving tribocorrosion performance of chemically bonded ceramic phosphate coating reinforced by GO-ZnO

To enhance the tribocorrosion properties of chemically bonded phosphate ceramic coating (CBPCC), GO-ZnO was prepared and added into CBPCC. And the tribocorrosion behaviour of CBPCC was investigated. Results show that, with the introduction of GO-ZnO, the open circuit potential of CBPCC shifts in a positive direction and corrosion current density decreases. In addition, the total material loss, the total mechanical wear loss and the total electrochemical corrosion loss of CBPCC all decrease with the increase of GO-ZnO. The wear track of CBPCC after tribocorrosion without GO-ZnO is rough and porous, while the wear track becomes smooth and dense with the incorporation of GO-ZnO. The material in wear track is anchored by GO-ZnO due to the strong bond between GO-ZnO and CBPCC, which decreases the wear loss. Because of the extra force from the tribocorrosion experiment, the material anchored by GO-ZnO forms to a dense structure which prevents electrolyte diffusion into CBPCC. Moreover, GO-ZnO can block the electrolyte diffusion pathway and make it more tortuous. The resistance to the electrolyte diffusion decreases the corrosion current density and the increased wear loss due to electrochemical corrosion.     

Features of crystal structures and thermo-mechanical properties of weberites RE3NbO7 (RE=La,Nd, Sm,Eu, Gd) ceramics

The features of crystal structures, thermo-mechanical properties and their dominant mechanisms of weberites RE₃NbO₇ were studied as high-temperature oxides. We concentrated on connections between structures and thermo-mechanical properties, the influences of bond lengths, lattice distortion degrees and microstructures on these properties were estimated. The shortening of bond length and increment of bonding strength would lead to the increase of mechanical properties. The Vickers hardness (4.5-7.8 GPa) and toughness (0.5-1.6 MPa·m^1/2) of weberites RE₃NbO₇ are enhanced by grain refinement and increment of bond strength, while crystal structures, bond lengths, and lattice distortion degrees influenced their Young's modulus (100-170 GPa). Nano-indentation was applied to test the influence of microstructures on modulus and hardness. The dominant mechanisms for mechanical properties and thermal conductivity were proposed, which was conducive to properties tailoring and engineering applications of weberites RE₃NbO₇ oxides.     

Rational Designs for Lithium-Sulfur Batteries with Low Electrolyte/Sulfur Ratio

Lithium-sulfur batteries (LSBs) are considered a promising next-generation energy storage device owing to their high theoretical energy density. However, their overall performance is limited by several critical issues such as lithium polysulfide (PS) shuttles, low sulfur utilization, and unstable Li metal anodes. Despite recent huge progress, the electrolyte/sulfur ratio (E/S) used is usually very high (≥20 µL mg⁻¹), which greatly reduces the practical energy density of devices. To push forward LSBs from the lab to the industry, considerable attention is devoted to reducing E/S while ensuring the electrochemical performance. To date, however, few reviews have comprehensively elucidated the possible strategies to achieve that purpose. In this review, recent advances in low E/S cathodes and anodes based on the issues resulting from low E/S and the corresponding solutions are summarized. These will be beneficial for a systematic understanding of the rational design ideas and research trends of low E/S LSBs. In particular, three strategies are proposed for cathodes: preventing PS formation/aggregation to avoid inadequate dissolution, designing multifunctional macroporous networks to address incomplete infiltration, and utilizing an imprison strategy to relieve the adsorption dependence on specific surface area. Finally, the challenges and future prospects for low E/S LSBs are discussed.     

M- S-H formation in MgO-SiO2slurries via wet milling for magnesia based castables

It is believed that the formation of hydration phase, MgO-SiO₂-H₂O (M-S-H), contributes to good workability and reliable comprehensive properties for magnesia based castables. In order to stimulate the formation of M-S-H in magnesia based castables and understand the minimum introduction of microslica amount, wet milling process was used to promote the dissolution of MgO and SiO₂ in this work. The slurry containing different content of microsilica with wet milling technology and the castables with/without wet milling slurry were prepared. The effects of microsilica content on the formation of hydration phases were analyzed by XRD, FT-IR and TG/DSC and the properties of magnesia based castables were evaluated by explosion resistance, CMOR, HMOR and so on. The results showed that the formation of M-S-H was accelerated because of the dissolution of Mg²⁺ and HSiO₃^? in wet milling process. Higher amount of M-S-H led to a tight bonding in the early stage, and a denser structure after firing at high temperature due to the limited formation of brucite and in-situ formation of evenly distributed forsterite phase. In addition, much higher HMOR were obtained when less microsilica was added, attributing to the suppressed formation of low-melting-point liquid. Therefore, 2–3 wt% microsilica addition was recommended in this process.     

Chromaticity-tunable remote LuYAG: Ce phosphor-in-glass film on regular textured glass substrate for white light emitting diodes

All inorganic remote phosphor-in-glass film exhibits excellent properties in high power white light-emitting-diodes (WLEDs) thanks to their easy fabrication and thermal stability. Herein, fabrication of (Lu, Y)₃Al₅O₁₂: Ce³⁺ (LuYAG: Ce)phosphors embedded in borosilicate glass film by the conventional solid state reaction and spin coating technology has been reported. The introduction of Y³⁺ ions reduces the difference of relative growth rate along some directions in growth of LuYAG microparticles, yielding a finer grain with smooth edges. By adjusting the molar concentration of Y³⁺ ions in LuAG phosphor, a series of tunable broadband emission from green to yellow region is observed and maintains excellent thermal stability. Meanwhile, the decay curves of samples with different Y³⁺ are almost same. SEM images show that phosphor particles are homogenously distributed within the glass matrix and keep their original morphology, suggesting the phosphor-in-glass films were synthesized as expected. Finally, a simple WLEDs based on the films was constructed using the commercial blue chip. The correlated color temperature ranging from 4853K to 4627K and high color rendering index from 81.4–79.7 were obtained. Upon the different driving current, the chromaticity coordinates of as-fabricated film exhibit good light color stability. These results bring an inspiring insight to tune the luminescent performance for remote WLEDs.     

基于大数据的电网公司安全生产数据分析平台设计

本文基于大数据视角设计了电网公司安全生产数据分析平台.通过平台挖掘分析电网公司实时运行数据信息,可全方位充分掌握公司安全生产状态,还可及时发现、共同解决不符合公司发展需要的相关问题,对于公司安全生产与长远稳定发展发挥着重要作用.通过研究表明,安全生产数据分析平台的设计可推动电网公司创新改革安全生产管理模式,切实整合信息资源,提高安全生产水平,实现精益化运营;而明确的平台发展定位与功能优化设计,可确保安全生产数据分析平台高效稳定运转.     

Vibrational Spectroscopic Investigation of Blood Plasma and Serum by Drop Coating Deposition for Clinical Application

In recent decades, vibrational spectroscopic methods such as Raman and FT-IR spectroscopy are widely applied to investigate plasma and serum samples. These methods are combined with drop coating deposition techniques to pre-concentrate the biomolecules in the dried droplet to improve the detected vibrational signal. However, most often encountered challenge is the inhomogeneous redistribution of biomolecules due to the coffee-ring effect. In this study, the variation in biomolecule distribution within the dried-sample droplet has been investigated using Raman and FT-IR spectroscopy and fluorescence lifetime imaging method. The plasma-sample from healthy donors were investigated to show the spectral differences between the inner and outer-ring region of the dried-sample droplet. Further, the preferred location of deposition of the most abundant protein albumin in the blood during the drying process of the plasma has been illustrated by using deuterated albumin. Subsequently, two patients with different cardiac-related diseases were investigated exemplarily to illustrate the variation in the pattern of plasma and serum biomolecule distribution during the drying process and its impact on patient-stratification. The study shows that a uniform sampling position of the droplet, both at the inner and the outer ring, is necessary for thorough clinical characterization of the patient’s plasma and serum sample using vibrational spectroscopy.